作 者:喻威[1] 刘升[1] 杭乃勤[1] 李浩进[1] 孙志亮[1]
机构地区:[1]武汉科技大学材料与冶金学院,武汉430081
出 处:《特殊钢》2011年第1期30-33,共4页Special Steel
摘 要:钢厂轧制U75V钢(%:0.71~0.80C、0.50~0.80Si、0.70~1.05Mn、0.04~0.12V、0.23Cu)60 kg/m重轨的铸坯尺寸为380 mm×280 mm,经第2架粗轧后坯料的断面面积为18 015 mm^2。通过轧制变形试验和显微镜观察测试,结合生产现场技术参数建立了有限元模型,以研究分析轧制变形对脱碳层影响。得出经第1粗轧机架和第2粗轧机架孔型轧制后,轨头脱碳层从1.2mm降至0.53 mm,轨腰脱碳层从1.5 mm降至0.54 mm,轨底脱碳层从1.5 mm降至0.83 mm。实测成品轨头的脱碳层为0.2 mm。The section size of casting bloom to roll 60 kg/m heavy rail of steel U75V(%:0.71~0.80C,0.50~0.80Si,0.70~1.05Mn,0.04~0.12V,0.23Cu) is 380 mm×280 mm and the section area of rolled piece out of second stand rougher mill is 18 015 mm^2.A finite element model is established by rolling deformation test and microscopic observation and measure combining with technical parameters at production situs to study and analyze the effect of rolling deformation on depth of decarburized layer of heavy rail.It is obtained that as the bloom is rolled by primary stand mill and second stand rougher mill,decarburized layer of rail head decreases to 0.53 mm from 1.2 mm,decarburized layer of rail waist decreases to 0.54 mm from 1.5 mm and decarburized layer of rail bottom decreases to 0.83 mm from 1.5 mm.The measured decarburized layer of finished rail head is 0.2 mm.
分 类 号:TG335[金属学及工艺—金属压力加工]
正在载入数据...
正在载入数据...
正在载入数据...
正在载入数据...
正在载入数据...
正在载入数据...
正在载入数据...
正在链接到云南高校图书馆文献保障联盟下载...
云南高校图书馆联盟文献共享服务平台 版权所有©
您的IP:216.73.216.229