机械研磨在HDDR NdFeCoAlB磁粉中的作用  

Effects of mechanical milling in HDDR NdFeCoAlB magnetic powder

作　　者：罗玉亮[1] 林培豪[1] 杨涛[1] 

机构地区：[1]桂林电子科技大学材料科学与工程学院,广西桂林541004

出　　处：《磁性材料及器件》2011年第1期72-75,78,共5页Journal of Magnetic Materials and Devices

基　　金：广西自然科学基金资助项目(0310001)

摘　　要：采用机械研磨与HDDR相结合的方法制备NdFeCoAlB各向异性磁粉,并研究了机械研磨对NdFeCoAlB磁性能和磁各向异性的影响。结果表明,机械研磨可以制备出超细各向异性磁粉,球磨工艺对磁粉的HDDR工艺有较大影响;磁粉变细,可以降低磁粉的HD温度以及缩短HD、DR时间,球磨0.5h对应的最佳HDDR工艺为,HD:800℃×2h,DR:850℃×10min;球磨1、2、4h的磁粉最佳工艺为,HD:700℃×1h,DR:850℃×10min。球磨0.5h对应最佳工艺时材料的磁性能:Br=0.9670T,Hcj=763.8kA/m,DOA=0.32。Mechanical milling （MM） followed by HDDR was adopted to prepare anisotropic magnetic powder of NdFeCoA1B. The effects of MM on the magnetic properties and anisotropy of NdFeCoA1B magnetic powder were studied. The results showed that by MM ultrafine anisotropic magnetic powder can： be prepared, and the milling technology has great impact on HDDR magnetic powder; for thinner magnetic powder, the HD temperature and HD and DR time can be decreased. The optimum process of MM 0.Sh magnetic powder is： HD： 800℃×2h, DR： 850℃ × 10min; the optimum process of MM lh, 2h and 4h magnetic powder is： HD： 700℃×lh, DR： 850℃×10min. The magnetic properties ofMM 0.5h material corresponding to optimum process are： Br=0.9670T, Hcj=763.8kA/m, DOA=0.32.

关 键 词：HDDR NdFeCoAlB磁粉 机械研磨 各向异性 磁性能 

分 类 号：TM271.3[一般工业技术—材料科学与工程]