铝合金表面金黄色转化膜的研究  

Study on a Golden-yellow Conversion Coating on Aluminum Alloy

作　　者：许龙[1] 郭瑞光[1] 唐长斌[1] 张建国[1] 

机构地区：[1]西安建筑科技大学环境与市政工程学院,西安710055

出　　处：《表面技术》2011年第1期78-80,共3页Surface Technology

基　　金：教育部高等学校博士学科点专项科研基金(20096120110007);陕西省自然科学研究计划项目(SJ08-ZT05)

摘　　要：采用无毒高锰酸钾进行转化处理,在铝合金表面制备金黄色无铬转化膜。通过研究转化液组成和操作条件对转化处理效果的影响,确定了最佳处理工艺。经中性盐雾试验、扫描电镜(SEM)和能谱仪(EDS)分析测试了转化膜的耐蚀性、形貌和组成。研究结果表明,采用该工艺可获得耐蚀性能良好、颜色亮丽的金黄色转化膜。Non-toxic potassium permanganate was used to prepare a golden-yellow chromium-free conversion coating on aluminum alloy.Effects of solution composition and operation conditions on appearance and corrosion resistance of conversion coating was investigated,the optimum treatment process was obtained.The corrosion resistance,surface morphology and element constituents of the coating were investigated by neutral salt spray test,scanning electron microscopy（SEM） and energy dispersive spectrometer（EDS）.The results show that the process can obtain a bright golden yellow conversion coating with good corrosion resistance.

关 键 词：铝合金 金黄色转化膜 无铬 耐蚀性 

分 类 号：TG174.451[金属学及工艺—金属表面处理]