半无头轧制超长铸坯均热制度优化  

Reheating Schedule Optimization of Super-long Slab for Semi-endless Rolling

作　　者：康永林[1] 陈林恒[1] 赵显蒙[1] 刘旭辉[2] 周明伟[2] 成小军[2] 

机构地区：[1]北京科技大学材料科学与工程学院,北京100083 [2]涟源钢铁集团有限公司,湖南娄底417009

出　　处：《轧钢》2010年第6期1-4,共4页Steel Rolling

摘　　要：针对涟钢半无头轧制过程中超长铸坯纵向温度不均的问题,分析了其主要原因,并提出了解决超长铸坯纵向温差过大的可行性措施,指出最佳措施是在不影响生产节奏的前提下保证铸坯尾部在均热炉内的最短均热时间,并据此确定临界辊道传输速度。试验结果表明,采用优化后的均热制度,铸坯头尾温差可控制在30℃以内。To the longitudinal temperature non-uniform phenomenon of super-long slab during semi-endless rolling process in Lianyuan Iron Steel Co.,Ltd.,the main reasons are analyzed,and the feasible measures to improve the temperature uniformity are put forward.It is concluded that the optimum way to solve the problem is to make sure the minimum soaking time of casting slab tail,and correspondingly identify the critical transfer speed on condition that the production rhythm is not disturbed.Experimental result shows that temperature difference between the head and tail of the slab can be controlled within 30°C by adopting optimal reheating schedule.

关 键 词：半无头轧制 超长板坯 均热制度 

分 类 号：TG335[金属学及工艺—金属压力加工]