热处理对2A97铝锂合金轧板微观组织与力学性能的影响  

Effect of heat treatment on microstructure and mechanical properties of rolled 2A97 Al-Li alloy plate

作　　者：孙刚[1] 苏海[2] 高文理[2] 刘洪波[2] 陆政[1] 冯朝辉[1] 张显峰[1] 

机构地区：[1]北京航空材料研究院,北京100095 [2]湖南大学材料科学与工程学院,湖南长沙410082

出　　处：《金属热处理》2011年第2期74-78,共5页Heat Treatment of Metals

摘　　要：研究了新型高强2A97铝锂合金在不同的热处理状态下的微观组织及力学性能。结果表明:轧制态2A97铝锂合金经过热处理后,硬度得到了大幅度提高;520℃×80 min固溶+165℃×30 h时效处理,布氏硬度值高达187 HB,抗拉强度为510 MPa,伸长率为8%;时效初期硬度下降,出现回归现象,随着时效时间延长,合金硬度逐步升高,时效30 h,硬度接近峰值。Microstructure and mechanical properties of the high strength 2A97 Al-Li alloy were studied under different heat treatment.The results show that after heat treatment,the hardness of the rolled 2A97 Al-Li alloy increases greatly.After 520 ℃×80 min（solution）＋165 ℃×30 h（aging） treatment,the Brinell hardness can be up to 187 HB,the tensile strength is 510 MPa and the elongation reaches 8%.At the early aging stage,the hardness decreases and regression phenomenon appears;with prolonging aging time,the hardness gradually increases,and reaches to the peak until 30 h.

关 键 词：2A97铝锂合金 热处理 组织与性能 

分 类 号：TB331[一般工业技术—材料科学与工程]