铜含量对TSCR工艺生产取向硅钢热轧织构的影响  

Effect of Cu Content on Hot Rolling Texture of Grain Oriented Silicon Steel Produced by TSCR

作　　者：裴英豪[1,2] 刘锐[1] 陈其安[1] 唐广波[1] 彭云[1] 

机构地区：[1]钢铁研究总院,北京100081 [2]马鞍山钢铁股份有限公司,安徽马鞍山243000

出　　处：《钢铁研究学报》2011年第1期20-25,共6页Journal of Iron and Steel Research

基　　金：国家"十一五"科技支撑计划资助项目(2006BAE03A14)

摘　　要：取向硅钢热轧板中织构梯度对发展完善的二次再结晶十分关键,通过添加铜可以显著降低取向硅钢板坯加热温度,从而影响热轧板织构分布。利用X射线衍射仪,分析了实验室模拟薄板坯连铸连轧(TSCR)工艺的3种不同铜含量的取向硅钢热轧板织构。结果表明:不同铜含量热轧板表面到厚度1/4处均为弱的热轧织构,热轧板心部主要为{100}面织构;铜含量约在0.4%时,热轧板次表层的{110}<001>织构比例最高,而热轧板心部的{100}<110>织构比例最低;铜含量对热轧织构中{114}<110>和{001}<100>织构发展有显著影响。The texture gradient in hot rolled grain oriented silicon steel strip is one of the essential factors to achieve a perfect secondary recrystallization. The addition of copper can significantly reduce the slab reheating temperature of grain oriented silicon steel, so as to impact the texture distribution in the hot rolled strip. The texture of hot rolled grain oriented silicon steel strip as-rolled by thin slab casting and rolling process （TSCR） in laboratory with three different copper contents was analyzed by using X-ray diffraction tester. The results show that the main texture from the surface to 1/4 thickness in the hot rolled strip of different copper contents is the weak hot rolling texture, and the main texture in the center is { 100 } texture. When the copper content is about 0.4 %, the fraction of {110}〈001〉 texture in the near surface layer of hot rolled strip is highest, while the fraction of {100 } 〈 110〉 texture in the center of hot rolled strip is lowest. The copper content may significantly influence the development of { 114} 〈110〉 and { 001 } 〈100〉 textures in hot rolled grain oriented silicon steel strip.

关 键 词：取向硅钢 铜含量 热轧织构 薄板坯连铸连轧 

分 类 号：TG335.11[金属学及工艺—金属压力加工]