水对硬质聚氨酯泡沫塑料性能的影响研究  

RESEARCH ON THE EFFECT OF H_2O ON THE PROPERTIES OF THE RIGID POLYURETHANE FOAM

作　　者：韩海军[1] 丁雪佳[1] 张丽娟[1] 张德强[1] 褚文娟[1] 袁圆[1] 

机构地区：[1]北京化工大学北京市新型高分子材料制备与加工重点实验室,北京100029

出　　处：《工程塑料应用》2011年第1期18-20,共3页Engineering Plastics Application

基　　金：科技部科技人员服务企业行动项目(2009GJA1004508)

摘　　要：采用一步法合成了硬质聚氨酯泡沫塑料(PUF-R),考察了水的用量对PUF-R的表观芯密度、导热系数、拉伸强度、弯曲强度、压缩强度等性能影响,并利用扫描电子显微镜观察了泡孔形态。结果表明,随着水用量的增加,RPUF的密度、导热系数、拉伸强度、弯曲强度、压缩强度逐渐降低,储能模量随之下降,而泡孔直径则逐渐增大。One-step polymerization was adopted to synthesize the rigid polyurethane foam. Theeffeet of the amount of H2O on the apparent core density, tensile strength, bending strength, compressive strength and dynamic theology property of the material was investigated. In addition, the morphology of hole was observed by SEM. The results indicated that the density, heat conductivity, tensile strength, bending strength, compressive strength and storage modulus of rigid polyurethane foam plastics synthesized decreased with the amount of H2O increasing, while the diameter of the holes increased.

关 键 词：硬质聚氨酯泡沫塑料 发泡剂 力学性能 流变性能 

分 类 号：TQ328.3[化学工程—合成树脂塑料工业]