丙烯酸酯类加工助剂制备及其在硬质聚氯乙烯发泡制品中的应用  

Preparation of Acrylic Processing Additive and Its Application in Rigid PVC Foam Products

作　　者：李英[1,2] 赵占永 黄玉松 郑德 瞿雄伟[2] 

机构地区：[1]广东炜林纳功能材料有限公司,广东佛山528521 [2]河北工业大学高分子科学与工程研究所,天津300130

出　　处：《塑料工业》2011年第2期87-89,共3页China Plastics Industry

基　　金：河北省自然科学基金资助(E2010000107)

摘　　要：采用种子乳液聚合方法制备了核壳结构丙烯酸酯共聚物[PBA/Poly(MMA-co-St-co-FM-co-BA),PBMSF]胶乳,并考察了该共聚物的转化率、粒径大小及分布、特性黏数和平衡扭矩。结果表明,单体转化率高,无二次成核现象,最终乳胶粒粒径可控;获得的丙烯酸酯共聚物PBMSF的特性黏数高,明显提高了其与PVC共混物的平衡扭矩。这对于硬质PVC发泡制品的正常挤出过程是必需的,这种PBMSF加工助剂可防止泡孔的坍塌,满足工业使用条件。PBA/poly（MMA-co-St-co-FM-co-BA）, PBMSF, with core-shell structure was prepared by seeded emulsion polymerization. The transition rate, particle size, intrinsic viscosity and torque balance were researched. The results showed the monomer conversion was high. Threw was no secondary nucleation, and the latex particle size could be designed. Meanwhile, the intrinsic viscosity of PBMSF copolymer in chloroform was high, and the equilibrium torque was increased while blended with PVC resin. Extrusion of rigid foam was the most demanding PVC process in terms of melt strength to avoid a collapse of the cells. Finally, the PBMSF process additive met the industrial requirements.

关 键 词：聚丙烯酸酯 乳液聚合 加工助剂 聚氯乙烯 硬质发泡 

分 类 号：TQ328.2[化学工程—合成树脂塑料工业]