Growth,Structure,and Spectroscopic Characteristics of the Nd^(3+):LiGd(WO_4)_2 Crystal  

作　　者：黄新阳 王国富 

机构地区：[1]Institute of Research on the Functional Matter,Jiangxi University of Finance and Economy [2]Institute of Research on the Structure of Matter,Chinese Academy of Sciences

出　　处：《Chinese Journal of Structural Chemistry》2011年第1期85-96,共12页结构化学（英文）

基　　金：Supported by the National Natural Science Foundation of China (No.60808033);Natural Science Foundation of Jiangxi Province (No.2008GZW0012)

摘　　要：The Nd^3＋：LiGd（WO4） 2 crystal with dimensions of 25mm×28mm×16mm was grown by the top-seeded solution growth method from the 60 mol% Li2W2O7 flux. LiGd（WO4） 2 crystallizes in the tetragonal system with space group I41/a（C4h^6） and cell parameters： a = 5.1986 and c = 11.2652A. The hardness is about 5.0 Mohs＇ scale. The specific heat is 0.40 J·g^-1·K^-1 at 50 oC. The thermal expansion coefficients for a-and c-axes are 1.314×10^-5 and 2.052×10^-5 K^-1,respectively. The room-temperature polarized absorption and emission spectra and the fluorescence decay curve was measured. The parameters of oscillator strengths,the spontaneous transition probabilities,the fluorescence branching ratios,the radiative lifetimes,and the emission cross sections have been investigated based on Judd-Ofelt theory and Füchtbauer-Ladenburg method. The absorption cross-section is 5.19×10^-20 cm^2 at 805 nm for π-polarization and its line width is 15 nm; the emission cross section is 1.726×10^-19 cm^2 at 1060.5 nm for π-polarization. The fluorescence and radiative lifetimes are 86 and 158 μs,respectively. The fluorescence quantum efficiency is 54.43%.The Nd^3＋：LiGd（WO4） 2 crystal with dimensions of 25mm×28mm×16mm was grown by the top-seeded solution growth method from the 60 mol% Li2W2O7 flux. LiGd（WO4） 2 crystallizes in the tetragonal system with space group I41/a（C4h^6） and cell parameters： a = 5.1986 and c = 11.2652A. The hardness is about 5.0 Mohs＇ scale. The specific heat is 0.40 J·g^-1·K^-1 at 50 oC. The thermal expansion coefficients for a-and c-axes are 1.314×10^-5 and 2.052×10^-5 K^-1,respectively. The room-temperature polarized absorption and emission spectra and the fluorescence decay curve was measured. The parameters of oscillator strengths,the spontaneous transition probabilities,the fluorescence branching ratios,the radiative lifetimes,and the emission cross sections have been investigated based on Judd-Ofelt theory and Füchtbauer-Ladenburg method. The absorption cross-section is 5.19×10^-20 cm^2 at 805 nm for π-polarization and its line width is 15 nm; the emission cross section is 1.726×10^-19 cm^2 at 1060.5 nm for π-polarization. The fluorescence and radiative lifetimes are 86 and 158 μs,respectively. The fluorescence quantum efficiency is 54.43%.

关 键 词：optical microscopy growth from melt Nd^3＋：LiGd（WO4）2 crystal solid state laser materials 