淬火温度对Cr5型冷轧工作辊用钢组织及性能的影响  

Influence of Quenching Temperature on Microstructure and Property of Cr5 Steel for Cold Roller

作　　者：唐志国[1] 李倩[1] 蔡大勇[1] 廖波[1] 

机构地区：[1]燕山大学亚稳材料制备技术与科学国家重点实验室,河北秦皇岛066004

出　　处：《热加工工艺》2011年第2期167-169,172,共4页Hot Working Technology

基　　金：河北省科技支撑计划资助项目(07212109D)

摘　　要：采用金相显微镜、扫描电镜、透射电镜和X射线衍射仪研究了淬火温度对Cr5型冷轧工作辊用钢组织及性能的影响。结果表明,调质态Cr5型冷轧工作辊用钢组织中的碳化物主要为Cr7C3型,较之球化退火态、调质态的碳化物更为细小,尺寸为100～300nm;对于调质态的Cr5钢,当淬火温度为875～950℃时,随淬火温度的升高,硬度单调上升;当淬火温度超过950℃时,硬度略有降低。The influences of quenching temperature on the microstructure and property of Cr5 steel for cold roller were studied by scanning electron microscopy,transmission electron microscopy and X-ray diffraction.The carbide in the microstructure of Cr5 steel after quenching and tempering treatment is mainly characterized as Cr7C3.Compared with the spheroidic annealing state,the carbide under quenching and tempering condition is refined,about 100～300 nm.The hardness increases monotonously after quenching at 875 ℃～950 ℃.By contrast,the hardness decreases when the quenching temperature above 950 ℃.

关 键 词：Cr5型冷轧工作辊 淬火温度 组织 

分 类 号：TG162.6[金属学及工艺—热处理]