聚甲醛熔体纺丝的流变性能研究  

Rheological behavior of polyformaldehyde during melt spinning process

作　　者：吴思蝶[1] 张国礼[2] 兰建武[1] 王焕莲[1] 王新雷[1] 

机构地区：[1]四川大学轻纺与食品学院,四川成都610065 [2]乌鲁木齐石化公司计划处,新疆乌鲁木齐830019

出　　处：《合成纤维工业》2011年第1期33-35,共3页China Synthetic Fiber Industry

基　　金：四川省科技支撑计划(2010FZ0015)

摘　　要：采用Rheograph2002高压毛细管流变仪测定了聚甲醛(POM)的流变性能。结果表明:在所研究的温度和剪切速率(γ)范围内,POM熔体为假塑性非牛顿流体,其表观粘度(η_a)随温度和γ的提高均降低;POM的η_a对温度的依赖关系服从Andrade公式,粘流活化能随γ的提高而降低;在220℃以下,熔融时间对POM的η_a的影响不大,可以对POM进行正常的熔融纺丝。The rheological behavior of polyformaldehyde （ POM ） was measured with a Rheograph 2002 capillary rheometer. The results showed that POM melt was pseudoplastic non-Newtonian fluid within the study range of shearing rate （ γ ） and temperature. The apparent viscosity （ ηa） of POM melt dropped with the elevation of temperature and γ. The dependence of ηa on temperature obeyed Andrade equation. The viscous flow activation energy decreased with the increase oft. The melting time had a slight effect on ηa of POM and the melt spinning process of POM proceeded smoothly below 220 ℃.

关 键 词：聚甲醛 流变性能 非牛顿流体 粘流活化能 表观粘度 

分 类 号：TQ340.1[化学工程—化纤工业]