铁基粉末冶金件双层辉光等离子Cr-Mo共渗研究  

Study on Mo-Cr Double Glow Plasma Surface Alloying of Iron-based Powder Metallurgical Product

作　　者：刘凯[1] 缪强[1] 胡超杰[1] 

机构地区：[1]南京航空航天大学材料科学与技术学院,江苏南京211100

出　　处：《金属功能材料》2011年第1期26-29,共4页Metallic Functional Materials

摘　　要：采用双层辉光等离子技术在对粉末冶金材料FN0205进行等离子烧结的同时在其表面进行Cr-Mo共渗处理。达到烧结效果的同时在试样表面得到合金渗层,渗层表面Cr含量达到10%左右,Mo含量达到5%左右。渗层厚度达到68μm。合金渗层表面物相由Fe、Fe-Cr、Cr23C6、Cr7C3、Mo2C组成。渗层表面显微硬度达到710 HV,硬度向内呈梯度分布。This paper deals with the composite treatment of hollow cathode plasma sintering and Cr-Mo plasma surface alloying on FN0205.Alloying layer can be formed on the surface when the sintering was implemented.The layer thickness reaches 68 μm and Cr,Mo contents reach to 10%,5% at surface layer.The phases of alloying layer consist of Fe,Fe-Cr,Cr7C3,Cr23C6,Mo2C.The micro-hardness of alloying layer reaches 710HV and a gradient distribution of micro-hardness is observed in the layer.

关 键 词：铁基粉末 等离子 双层辉光放电 合金化 

分 类 号：TG174.444[金属学及工艺—金属表面处理]