C_3S含量对阿利特-硫铝酸盐水泥熟料煅烧及性能的影响  

Influence of C_3S content on calcining and properties of alite-sulphoaluminate cement clinker

作　　者：李保亮[1] 李艳君[1] 吴远超[1] 刘通[1] 王卫山[1] 刘晓存[1] 

机构地区：[1]济南大学材料科学与工程学院,山东济南250022

出　　处：《水泥》2011年第3期9-12,共4页Cement

摘　　要：探讨了C3S含量对阿利特-硫铝酸盐水泥熟料煅烧及水泥性能的影响。结果表明:随C3S含量增加,生料的易烧性变差;C3S含量较高时,不利于C4A3S矿物的形成;随C3S矿物含量增多,水泥强度升高,凝结时间相应延长;C3S含量降低,水泥凝结时间缩短。The influence of the C3S content on the calcining and properties of alite-sulphoaluminate cement clinker was studied.The results showed that the burnability of raw meal would be worse and the strength of the cement would increase with the amount of C3S increasing,and the rate of formation could be influenced if the amount of C3S was high.The setting time of the cement were delayed remarkably with the amount of C3S increasing.

关 键 词：C3S 阿利特-硫铝酸盐水泥熟料 煅烧 矿物形成 水泥性能 