莫来石-刚玉多孔陶瓷膜支撑体的制备  

Fabrication of mullite-corundum porous ceramic membrane support

作　　者：韩火年[1,2] 李强[1,2] 洪昱斌 丁马太[2,4] 何旭敏[1] 蓝伟光[2,3] 

机构地区：[1]厦门大学化学化工学院,福建厦门361005 [2]厦门大学材料学院,福建厦门361005 [3]三达膜科技(厦门)有限公司,福建厦门361022 [4]龙岩学院化学与材料学院,福建龙岩364000

出　　处：《功能材料》2011年第3期425-428,431,共5页Journal of Functional Materials

摘　　要：通过沉淀法制备碳酸铝铵超细粉体均匀包裹的氧化铝粉体,煅烧后,继令其与纳米二氧化硅按一定比例球磨混合,预烧,添加适当的粘结剂和造孔剂,再经捏合、陈腐、挤出成型、烘坯、烧结,制备膜支撑体。结果表明,二氧化硅加入量为12%(质量分数)、1550℃烧结所得的膜支撑体综合性能较好:纯水通量为22.2m3/(m2·h);爆破压力为3.40MPa,开孔率为40.21%;经10%(质量分数)H2SO4或5%(质量分数)NaOH于100℃下浸渍36h后,爆破压力仍分别为2.67和2.89MPa,表明它还具有良好的耐酸碱性能。Prepared by precipitation method with aluminium nitrate and ammonium acid carbonate,after calcining,superfine powder coated alumina was ball-mill mixed with nano-silica in a certain proportion,then pre-sintered,an appropriate amount binder and pore-forming agent were added.After kneading,aging、extrusion molding and drying,the membrane supports were temperature-programming sintered to certain temperature and held for 2h.It is shown that support body with 12wt% SiO2 and sintered at 1550℃ has much better comprehensive functions： water flux is 22.21m3/（m2·h）,the bursting strength is 3.40MPa,and open porosity is 40.21%.After dipping in 10wt% H2SO4 or 5wt% NaOH for 36h at 100℃ respectively,the membrane support still has a bursting high up to 2.67MPa and 2.89MPa,it indicates that the acid resistance and alkaline resistance property of the membrane support is excellent.

关 键 词：沉淀法 多孔陶瓷膜支撑体 挤出成型 

分 类 号：R318[医药卫生—生物医学工程] TB332[医药卫生—基础医学]