Reduction of 1-3 mm Iron Ore by CO on Fluidized Bed  

作　　者：PANG Jian-ming GUO Pei-min ZHAO Pei 

机构地区：[1]The State Key Laboratory for Advanced Steel Processes and Products,Central Iron and Steel Research Institute,Beijing 100081,China

出　　处：《Journal of Iron and Steel Research International》2011年第3期1-5,共5页

基　　金：Item Sponsored by National Natural Science Foundation of China(50474006);National Key Technology Research and Development Programin 11th Five-Year Plan of China(2006BAE03A12,2006BAE03A05)

摘　　要：The reduction-degree of the sample increases and the utilization ratio of gas decreases when the reaction lasts longer time,which indicates that the reaction is faster at the beginning of reduction,while it becomes slower in subsequent process.The higher the reaction temperature,the higher the utilization ratio of gas and the reduction-degree are,but the difference of utilization ratio among the different temperatures becomes smaller with time.The utilization ratio of gas can reach about 8% and the reduction-degree is 80% for 20 min reduction at 850 ℃,indicating that the reduction reaction by CO is very fast at high temperature.The higher the reaction temperature,the higher the apparent reaction rate constant is,but the difference of apparent reaction rate constant among the different temperatures becomes bigger.The apparent activation energy is about 59.11 kJ/mol in the fluidized bed experiment.The increase of reduction-degree with gas velocity shows quite good linearity,indicating that at high temperature even higher velocity of reducing gas can be used to improve the productivity of reactor when CO is used as reducing gas.With the increase of charge height,the metallization ratio and the reduction-degree decrease,but the utilization ratio of gas increases.The reduction-degree of the sample increases and the utilization ratio of gas decreases when the reaction lasts longer time,which indicates that the reaction is faster at the beginning of reduction,while it becomes slower in subsequent process.The higher the reaction temperature,the higher the utilization ratio of gas and the reduction-degree are,but the difference of utilization ratio among the different temperatures becomes smaller with time.The utilization ratio of gas can reach about 8% and the reduction-degree is 80% for 20 min reduction at 850 ℃,indicating that the reduction reaction by CO is very fast at high temperature.The higher the reaction temperature,the higher the apparent reaction rate constant is,but the difference of apparent reaction rate constant among the different temperatures becomes bigger.The apparent activation energy is about 59.11 kJ/mol in the fluidized bed experiment.The increase of reduction-degree with gas velocity shows quite good linearity,indicating that at high temperature even higher velocity of reducing gas can be used to improve the productivity of reactor when CO is used as reducing gas.With the increase of charge height,the metallization ratio and the reduction-degree decrease,but the utilization ratio of gas increases.

关 键 词：CO fluidized bed fine powder iron ore reduction-degree 