分子链末端改性溶聚丁苯橡胶的结构与性能研究  

Structure and Properties of Chain-end Modified SSBR

作　　者：王雷[1] 张兴英[1] 赵素合[1] 

机构地区：[1]北京化工大学北京市新型高分子材料制备与加工重点实验室,北京100029

出　　处：《轮胎工业》2011年第3期152-158,共7页Tire Industry

摘　　要：采用阴离子活性/可控聚合方法制备了溶聚丁苯橡胶(SSBR)、大体积官能团叔丁基二苯基氯硅烷制备封端改性SSBR(T-SSBR)和锡偶联星形SSBR,并对其结构和性能进行研究。结果表明:与未改性SSBR硫化胶相比,T-SSBR和星形SSBR硫化胶的炭黑分散性较好,达到纳米填料纳米尺度的分散,滞后损失较小,动态力学性能较好,拉伸强度、拉断伸长率、撕裂强度和回弹值较大;与星形SSBR硫化胶相比,T-SSBR硫化胶的拉伸强度、拉断伸长率和撕裂强度较小,动态压缩疲劳温升较低,抗湿滑性能较好,抗动态切割性能略低。Solution polymerized styrene-butadiene rubber（SSBR）,SSBR with end-capping modification（T-SSBR） by tert-butylchlorodiphenylsilane（large volume functional groups） and star-shaped SSBR were prepared by living/controlled anionic polymerization,and the structure and properties of those SSBRs were investigated.The results showed that,compared with unmodified SSBR,the dispersion of carbon black in T-SSBR and star-shaped SSBR vulcanizates were better,and carbon black in T-SSBR and star-shaped SSBR vulcanizates achieved nano-scale dispersion,the hysteresis loss were lower,the dynamic properties were better,and the tensile strength,elongation at break,tear strength and resilience were better.Compared with star-shaped SSBR vulcanizate,the tensile strength,elongation at break and tear strength of T-SSBR vulcanizate were lower,the dynamic compression fatigue heat build-up was lower,the wet-skid resistance was better,and the dynamic cutting resistance was a little worse.

关 键 词：胎面胶 溶聚丁苯橡胶 炭黑 微观结构 动态力学性能 滚动阻力 

分 类 号：TQ333.1[化学工程—橡胶工业] TQ330.381