Gas Sensitivity of Poly (3, 4-ethylene dioxythiophene) Prepared by a Modified LB Film Method  

作　　者：郑华靖 

机构地区：[1]State Key Laboratory of Electronic Thin Films Integrated Devices, School of Optoelectronic Information, University of Electronic Science and Technology of China

出　　处：《Journal of Wuhan University of Technology(Materials Science)》2011年第1期70-74,共5页武汉理工大学学报（材料科学英文版）

基　　金：Funded by the National Natural Science Foundation of China (No.60372002)

摘　　要：An arachidic acid/poly （3, 4-ethylene dioxythiophene） （AA/PEDOT） multilayer Langmuir-Blodgett （LB） film was prepared by a modified LB film method. The theories were utilized to explain the effects between HCl molecule and LB film. The gas sensitivity mechanism of poly （3, 4-ethylene dioxythiophene） （PEDOT） multilayer film can be explained by the charge transfer between p system of PEDOT and oxidization HCl system. The gas sensitivity of PEDOT LB film deposited interdigital electrode to HCl was tested. The results showed that film thickness, treating temperature, deposition speed had different influence on film gas sensitivity. The AA/PEDOT film deposited device exhibited nonlinear behavior to HCl gas at lower concentration （20-60 ppm） and linear response behavior at higher gas concentration was observed. The time of the compound LB film of the AA/PEDOT responding to the 30 ppm HCl gas is about 20 seconds, which is far quicker than the time of the film to the PEDOTPRESS film（about 80 seconds）. It is not higher film press to better film. When the film press attains 45 mNs/m, the sensitivity of the AA/PEDOT film on the contrary descends.An arachidic acid/poly （3, 4-ethylene dioxythiophene） （AA/PEDOT） multilayer Langmuir-Blodgett （LB） film was prepared by a modified LB film method. The theories were utilized to explain the effects between HCl molecule and LB film. The gas sensitivity mechanism of poly （3, 4-ethylene dioxythiophene） （PEDOT） multilayer film can be explained by the charge transfer between p system of PEDOT and oxidization HCl system. The gas sensitivity of PEDOT LB film deposited interdigital electrode to HCl was tested. The results showed that film thickness, treating temperature, deposition speed had different influence on film gas sensitivity. The AA/PEDOT film deposited device exhibited nonlinear behavior to HCl gas at lower concentration （20-60 ppm） and linear response behavior at higher gas concentration was observed. The time of the compound LB film of the AA/PEDOT responding to the 30 ppm HCl gas is about 20 seconds, which is far quicker than the time of the film to the PEDOTPRESS film（about 80 seconds）. It is not higher film press to better film. When the film press attains 45 mNs/m, the sensitivity of the AA/PEDOT film on the contrary descends.

关 键 词：poly （3 4-ethylene dioxythiophene） （PEDOT） Langmuir-Blodgett （LB） film method gas sensitivity measurement 