Antiplasticizing Effect of MOCA on Poly(vinyl chloride)  

作　　者：张藕生 张超灿 

机构地区：[1]School of Materials Science and Engineering, Wuhan University of Technology

出　　处：《Journal of Wuhan University of Technology(Materials Science)》2011年第1期83-87,共5页武汉理工大学学报（材料科学英文版）

基　　金：Funded by National Natural Science Foundation of China(No.50673080)

摘　　要：An obvious antiplasticizing effect has been observed in PVC with small amount of MOCA, 3,3’-dichloro-4,4’-diamino-diphenylmethane. PVC-MOCA interaction and crystallization behavior of PVC/MOCA blends were investigated in detail to explain the mechanism of antiplasticization on the basis of a series of techniques including DMA, FTIR, and DSC. The results of mechanical properties tests show that the tensile strength of PVC with 5 phr of MOCA reaches a maximum value, 69.5 Mpa, which is about 23 % higher than that of pure PVC. The rise in tensile strength was attributed to an antiplasticizing effect of MOCA on PVC as confirmed by DMA measurements. The evidences from FTIR reveal that a strong hydrogen-bonding interaction takes place between the nitrogen atom of –NH2 groups in MOCA and the methine proton of PVC repeat units. The results of DSC analysis indicate that crystallization behavior of MOCA is suppressed completely and the crystallinity of PVC decreases with the increase of MOCA amount.An obvious antiplasticizing effect has been observed in PVC with small amount of MOCA, 3,3’-dichloro-4,4’-diamino-diphenylmethane. PVC-MOCA interaction and crystallization behavior of PVC/MOCA blends were investigated in detail to explain the mechanism of antiplasticization on the basis of a series of techniques including DMA, FTIR, and DSC. The results of mechanical properties tests show that the tensile strength of PVC with 5 phr of MOCA reaches a maximum value, 69.5 Mpa, which is about 23 % higher than that of pure PVC. The rise in tensile strength was attributed to an antiplasticizing effect of MOCA on PVC as confirmed by DMA measurements. The evidences from FTIR reveal that a strong hydrogen-bonding interaction takes place between the nitrogen atom of –NH2 groups in MOCA and the methine proton of PVC repeat units. The results of DSC analysis indicate that crystallization behavior of MOCA is suppressed completely and the crystallinity of PVC decreases with the increase of MOCA amount.

关 键 词：poly（vinyl chloride） MOCA ANTIPLASTICIZATION CRYSTALLINITY INTERACTION 

分 类 号：TQ325.3[化学工程—合成树脂塑料工业] TU242.5[建筑科学—建筑设计及理论]