热镀锌沉没辊轴套用PTA涂层耐蚀性的研究  

Research on Corrosion Resisting Properties of PTA Coating Used for Hot-dip Galvanized Sink Rolls Bushing

作　　者：万伟伟[1] 沈婕[1] 高峰[1] 侯伟骜[1] 国俊丰[1] 

机构地区：[1]北京矿冶研究总院,北京100044

出　　处：《热喷涂技术》2010年第3期60-65,共6页Thermal Spray Technology

摘　　要：在CoCrMo系合金、CoCrW系合金、铁基合金和镍基合金中添加硼化物、碳化物,采用等离子喷焊(PTA)的方法,在热镀锌沉没辊轴套上制备多种涂层。研究结果表明,在CoCrMo系合金中添加CrB2MoB的涂层,焊道成型性良好;涂层表面与锌液基本不浸润,腐蚀面平滑,耐蚀性最佳。Multiform coatings used for hot-dip galvanized sink rolls bushing are produced by PTA. Carbides and borides are added into CoCrMo-based alloy、CoCrW-based alloy、iron-based alloy and Ni-based alloy. The results show that good bead compactibility is obtained after CrB2MoB is added into CoCrMo-based alloy. And this coating with smooth corrosion surface and infiltrating to molten zinc has better corrosion resisting property than others.

关 键 词：等离子喷焊 耐熔锌腐蚀 CoCrMo系合金 喷焊成型性 

分 类 号：TG174.443[金属学及工艺—金属表面处理]