STUDY ON THE DRYING SHRINKAGE OF MAGNESIUM PHOSPHATE CEMENT MORTAR

作　　者：林玮[1] 孙伟[1] 李宗津[2] 

机构地区：[1]东南大学材料科学与工程学院,南京210096 [2]香港科技大学土木工程系

出　　处：《工业建筑》2011年第4期75-78,84,共5页Industrial Construction

摘　　要：系统研究磷酸镁水泥砂浆的干燥收缩性能,从氧化镁活性、水胶比、磷镁比、粉煤灰掺量和缓凝剂使用等方面研究了影响磷酸镁水泥砂浆干燥收缩的影响因素。研究采用DEMEC方法指出,磷酸镁水泥砂浆的干燥收缩随着氧化镁活性的降低、水胶比的提高、磷镁比的降低、粉煤灰掺量的降低和缓凝剂的使用而增大。同时,分析指出,自由水分的蒸发是干燥收缩产生的主要原因,指出粉煤灰对于抑制磷酸镁水泥砂浆干燥收缩的贡献。The drying shrinkage of magnesium phosphate cement mortar was studied in the paper,including the influence of reactivity of magnesia,water to binder ratio,magnesium to phosphorus ratio,fly ash content and usage of retarder on the drying shrinkage of magnesium phosphate cement mortar.The conclusions indicated that the drying shrinkage of magnesium phosphate cement mortar increased with the decreasing of the magnesia reactivity,magnesium to phosphorus ratio and fly ash content,increasing of the water to binder ratio and usage of retarder.And the analysis showed that the evaporation of free water is the main reason for drying shrinkage and fly ash content could restrain the drying shrinkage of magnesium phosphate cement mortar.

关 键 词：磷酸镁水泥 干燥收缩 粉煤灰 活性 

分 类 号：TU578.1[建筑科学—建筑技术科学]