RE对耐候钢中P偏析的影响  

Effect of RE on Phosphorus Macrosegregation of Weather-resisting Steel

作　　者：郭宏海[1] 宋波[1] 候立松 毛璟红[3] 赵沛 

机构地区：[1]北京科技大学冶金与生态工程学院,北京100083 [2]五矿有色金属股份有限公司,北京100044 [3]北京科技大学材料科学与工程学院,北京100083 [4]中国钢研科技集团公司,北京100081

出　　处：《稀土》2011年第2期53-57,共5页Chinese Rare Earths

基　　金：国家"973"计划项目资助(2004CB619107)

摘　　要：研究了在不同冷速下添加RE对耐候钢中P元素宏观偏析的影响。研究发现,在钢中添加0.060%～0.380%量的RE,其固溶量可以达到0.006%～0.017%,这部分固溶稀土可以起到微合金化的作用,能够明显细化枝晶,增加等轴晶率,可以明显改善耐候钢中P元素的宏观偏析。继续加入过量的RE并不能提高其固溶含量。The effect of RE on phosphorus macrosegregation of weather-resesting steel has been studied.The results indicated that the solid solution contents of RE were 0.006%～0.017% when the steel contained 0.060%～0.380% residual RE.The solution RE could play the role of microalloying,refinement dendritic and increasing equiaxial crystal rate,that could obviously relieve phosphorus macro-segregation of weather-resisting steel.But the solid solubility of RE couldn＇t be raised by adding more RE.

关 键 词：耐候钢 磷偏析 稀土 