大尺寸CLBO单晶的生长和性质研究  

Study of Growth and Properties on Large Size CLBO Crystals

作　　者：张秀荣[1] 张顺兴[1] 柴耀[1] 

机构地区：[1]中国科学院上海光学精密机械研究所,上海201800

出　　处：《人工晶体学报》1999年第4期346-349,共4页Journal of Synthetic Crystals

基　　金：国家自然科学基金

摘　　要：本文对生长大尺寸硼酸铯锂（ＣｓＬｉＢ６Ｏ１０ ，简称ＣＬＢＯ） 单晶的生长工艺进行了探索研究，采用顶部籽晶泡生法生长出尺寸为７０ ×２５ｍｍ 的ＣＬＢＯ透明晶体。测量了晶体的干涉图，计算其折射率变化为Δｎ～１ ．２ ×１０ － ５ ，晶体的光学质量接近于玻璃水平（ ～１０ － ６） 。测量ＣＬＢＯ单晶的结构及其光学特性。用１５ｍｍ ×１０ｍｍ ×７ｍｍ 的ＣＬＢＯ 样品，在锁模Ｎｄ∶ＹＡＧ 激光器上做倍频实验，获得了波长为５３２ｎｍ 的倍频光，其转换效率高达６０ ％ 以上。The growth technology of large size CsLiB 6O 10 (CLBO) crystal have been investigated.The CLBO crystals were grown by means of top seeded Kyropoulos techniques,and the crystal has been obtained 70mm in diameter and 25mm high. The interferogram,structure pattern and the optical properties of CLBO crystal were measured.The change of refractive index is Δ n =1.2×10 -5 ,get near glass.Using 15mm×10mm×7mm CLBO crystal,the green light output at 532nm were realized by doubling the 1064nm light wave generated from the lock mode Nd∶YAG laser.the conversing efficiency is 60%,the pulse width is 22ps.

关 键 词：硼酸铯锂 非线性光学晶体 CLBO 单晶 晶体生长 

分 类 号：O782[理学—晶体学] TN204[电子电信—物理电子学]