钨丝/非晶复合材料的冲击性能研究  

Impact property of W fiber reinforced amorphous composite material

作　　者：王振明[1,2] 史洪刚[1,2] 冯宏伟[1,2] 尚福军[1] 祝理君[1] 苏继红[1] 

机构地区：[1]中国兵器科学研究院宁波分院,浙江宁波315103 [2]装甲与反装甲材料技术国防科技重点实验室,浙江宁波315103

出　　处：《兵器材料科学与工程》2011年第2期77-79,共3页Ordnance Material Science and Engineering

摘　　要：对钨丝增强锆基非晶复合材料在不同温度下的冲击性能进行试验,研究钨丝非晶复合材料的断裂方式,与钨合金比较两者不同的断口形貌。结果表明,钨丝/非晶复合材料冲击韧性低于钨合金,但其受低温影响较小,在-40℃下的冲击功和常温相比基本不变。冲击断口主要有钨丝和非晶基体的剥离,非晶基体的断裂,钨丝的断裂(其中钨丝在横向断裂时有时伴有纵向裂纹)3种断裂方式。Impact experiment of the W fiber reinforced amorphous composite material was made at different temperature.Comparison of fracture mode and feature with tungsten alloy was made.The results show that the impact proterty of W fiber amorphous composite material is lower than that of tungsten alloy and it is not affected by low temperature.The fracture of W fiber amorphous composite material includes three patterns：the peeling of W fiber from amorphous alloy;the fracture of amorphous alloy;the fracture of W fiber,with longitudinal crack sometimes.

关 键 词：钨丝增强锆基非晶复合材料 钨合金 冲击性能 断裂模式 

分 类 号：TB331[一般工业技术—材料科学与工程]