W-Ni-Fe系纳米复合粉体的制备工艺研究  

Preparation process of W-Ni-Fe nano powders

作　　者：逯庆国[1] 李明利[1,2] 周宇松[1] 周春江[1] 刘正伟[1] 

机构地区：[1]中国兵器科学研究院宁波分院,浙江宁波315103 [2]硅材料国家重点实验室,浙江大学材料科学与工程系,浙江杭州310027

出　　处：《兵器材料科学与工程》2011年第2期90-93,共4页Ordnance Material Science and Engineering

摘　　要：选择W-Ni-Fe系作为高密度钨合金材料体系,采用溶胶-凝胶方法制备出纳米氧化物复合粉体,用化学气相还原制备得到W-Ni-Fe系纳米复合粉体,研究了添加表面活性剂、还原温度、还原时间等工艺参数对粉体形貌粒径等物化性能的影响,确定了最佳工艺参数。The W-Ni-Fe compounds were chosen as high density tungsten alloy.The nano oxide powder of W-Ni-Fe was prepared by sol-gel method and then the powder was reduced by chemical reduction method.The influence of temperature,heat treat time and surfactant on the morphology and size of the powder was researched.The optimal process parameters were determined.

关 键 词：钨合金 溶胶-凝胶法 化学气相还原 纳米复合粉体 

分 类 号：TF841.1[冶金工程—有色金属冶金]