Annealing Effect on Transport and Magnetic Properties of La_(0.67)Sr_(0.33)MnO_3 Thin Films Grown on Glass Substrates by RF Magnetron Sputtering  

作　　者：Shaojie Fang Zhiyong Pang Fenggong Wang Liang Lin Shenghao Han 

机构地区：[1]School of Physics, State Key Laboratory of Crystal Materials, Shandong University, Jinan250100, China [2]School of Space Science and Applied Physics, Shandong University at Weihai, Weihai 264209, China

出　　处：《Journal of Materials Science & Technology》2011年第3期223-226,共4页材料科学技术（英文版）

基　　金：financial support from the National Natural Science Foundation of China (Grants No. 10974118);Shandong Province Natural Science Foundation (ZR2009GQ010);Scientific and Technological Developing Scheme of Shandong Province (Grant No.2008GG30004004);the Independent Innovation Foundation of Shandong University (IIFSDU,2010TS056)

摘　　要：The manganite La0.67Sr0.33MnO3 （LSMO） thin films were grown on glass substrates in a mixed argon and oxygen atmosphere by using RF magnetron sputtering. The structural characteristics, transport behaviors and magnetic properties of LSMO films were studied by annealing the films in air at 550 and 620℃. The out-of-plane lattice parameter αLSMO contracted after annealing and was close to that of bulk LSMO abulk, indicating that the internal strain was fully relaxed. Nanocrystalline grains were observed in the annealed films. Enhanced saturation magnetization and metal-to-insulator transition temperature （TMI=268 K） were also obtained. Curie temperatures （Tc） of the as-grown films was 340 K with the same as that of annealed at 550℃, but dropped to 315 K when the annealing temperature increased to 620℃, which can be attributed to the oxygen release during annealing in atmosphere.The manganite La0.67Sr0.33MnO3 （LSMO） thin films were grown on glass substrates in a mixed argon and oxygen atmosphere by using RF magnetron sputtering. The structural characteristics, transport behaviors and magnetic properties of LSMO films were studied by annealing the films in air at 550 and 620℃. The out-of-plane lattice parameter αLSMO contracted after annealing and was close to that of bulk LSMO abulk, indicating that the internal strain was fully relaxed. Nanocrystalline grains were observed in the annealed films. Enhanced saturation magnetization and metal-to-insulator transition temperature （TMI=268 K） were also obtained. Curie temperatures （Tc） of the as-grown films was 340 K with the same as that of annealed at 550℃, but dropped to 315 K when the annealing temperature increased to 620℃, which can be attributed to the oxygen release during annealing in atmosphere.

关 键 词：LA0.67SR0.33MNO3 ANNEALING Magnetron sputtering NANOCRYSTALLINE 

分 类 号：O484.1[理学—固体物理] TB383[理学—物理]