微量Ti对铸造镁合金组织及性能的影响  

Effect of Trace Ti on Microstructure and Properties of As-cast Mg Alloy

作　　者：王雪怡[1] 王智民[1] 郑育前[1] 曹永智[1] 

机构地区：[1]西安理工大学材料学院,陕西西安710048

出　　处：《热加工工艺》2011年第7期25-27,共3页Hot Working Technology

摘　　要：以AZ102镁合金为研究对象,分析微量Ti对其组织、性能的作用机理,并对Ti的分布进行了分析。结果表明:Ti主要分布在α-Mg和β-Mg17Al12之间;随着Ti含量从0.1wt%到0.4wt%,合金铸态组织和晶粒尺寸显著减小,使抗拉强度达到232.7 MPa。The effects of trace Ti on the microstructure and mechanical property of AZ102 alloy were investigated. The distribution of Ti was analyzed by EDS. The results show that Ti mainly distributes between α-Mg and β-Mg17Al12, the microstructure and grain size of as-cast alloy is remarkably refined with the increase of Ti content when the content of Ti increases from 0.1% to 0.4% （mass fraction）. So the tensile strength of the alloy can reach 232.7 MPa.

关 键 词：AZ102镁合金 钛 晶粒细化 显微组织 EDS 力学性能 