Effect of Nano-ZrO_2 on Microstructure and Thermal Shock Behaviour of Al_2O_3/SiC Composite Ceramics Used in Solar Thermal Power  

作　　者：徐晓虹 

机构地区：[1]School of Materials Science and Engineering,Wuhan University of Technology

出　　处：《Journal of Wuhan University of Technology(Materials Science)》2011年第2期285-289,共5页武汉理工大学学报（材料科学英文版）

基　　金：Funded by "973 Program" (2010CB227100)

摘　　要：The Al2O3-ZrO2（3Y）-SiC composite ceramics used in solar thermal power were prepared by micrometric Al2O3,nano-ZrO2 and SiC powders under the condition of pressureless sintering.The bulk density and bending strength of samples with 10vol% nano-ZrO2 sintered at 1480℃ were 3.222 g/cm3 and 160.4MPa,respectively.The bending strength of samples after 7 times thermal shock tests （quenching from 1000℃ to 25℃ in air medium） is 132.0MPa,loss rate of bending strength is only 17%.The effect of nano-ZrO2 content on the microstructure and performance of Al2O3-ZrO2（3Y）-SiC composite ceramic was investigated.The experimental results show that the bending strength of samples with above 10vol% nano-ZrO2 content has decreased,because the volume expansion resulting from t-ZrO2 to m-ZrO2 phase transformation is excessive;Adding proper nano-ZrO2 would be contributed to improve the thermal shock resistance of the composite ceramics.The Al2O3-ZrO2（3Y）-SiC composite ceramic has promising potential application in solar thermal power.The Al2O3-ZrO2（3Y）-SiC composite ceramics used in solar thermal power were prepared by micrometric Al2O3,nano-ZrO2 and SiC powders under the condition of pressureless sintering.The bulk density and bending strength of samples with 10vol% nano-ZrO2 sintered at 1480℃ were 3.222 g/cm3 and 160.4MPa,respectively.The bending strength of samples after 7 times thermal shock tests （quenching from 1000℃ to 25℃ in air medium） is 132.0MPa,loss rate of bending strength is only 17%.The effect of nano-ZrO2 content on the microstructure and performance of Al2O3-ZrO2（3Y）-SiC composite ceramic was investigated.The experimental results show that the bending strength of samples with above 10vol% nano-ZrO2 content has decreased,because the volume expansion resulting from t-ZrO2 to m-ZrO2 phase transformation is excessive;Adding proper nano-ZrO2 would be contributed to improve the thermal shock resistance of the composite ceramics.The Al2O3-ZrO2（3Y）-SiC composite ceramic has promising potential application in solar thermal power.

关 键 词：AL2O3 NANO-ZRO2 transformation toughening thermal shock resistance composite ceramics solar thermal power 

分 类 号：TF124.5[冶金工程—粉末冶金]