不同工艺制备硫酸钾插层膨润土缓释性能研究  

Study on slow-releasing performance of potassium sulfate insert in bentonite by different processes

作　　者：邹榕[1] 崔艳杰[1] 周莹[1] 梁玉祥[1] 

机构地区：[1]四川大学化工学院,四川成都610065

出　　处：《应用化工》2011年第4期572-578,共7页Applied Chemical Industry

基　　金：国家自然科学基金资助项目(50872085)

摘　　要：研究比较了由不同工艺制备硫酸钾并于膨润土层间插层、结晶、缓释。结果表明,碳酸钾制硫酸钾最佳工艺为:温度80℃,搅拌速度为1.5 m/s,搅拌时间30 min,矿浆浓度为20 g/100 mL;硫酸铵制硫酸钾最佳工艺条件为:配料比1.1∶1(摩尔比)、搅拌速度2.0 m/s,搅拌时间80 min,矿浆浓度25 g,乙醇浓度40%。The method of making potassium sulfate was compared by potassium carbonate and by sulfate-ammonium.The best technology conditions were obtained as follows：stirring speed 1.5 m/s,stirring time 30 min,pulp concentration 20 g/100 mL and the temperature of water bath 80 ℃.The best conditions from（NH4）2SO4 were as follows：the molar ratio of（NH4）2SO4 ∶KCl 1.1 ∶1,stirring speed 2.0 m/s,stirring time 80 min,pulp concentration 25 g and the concentration of ethanol 40%.

关 键 词：硫酸钾 膨润土 插层 

分 类 号：TQ050.4[化学工程]