新型可降解聚富马酸硅基酯的合成与表征  

Synthesis and characterization of new degradable poly(fumaric acid silyl ester)

作　　者：周德杰[1] 韩念凤[1] 唐新德[1] 刘宗林[2] 

机构地区：[1]山东交通学院新材料研究所,山东济南250357 [2]山东大学化学与化工学院,山东济南250100

出　　处：《合成橡胶工业》2011年第3期190-192,共3页China Synthetic Rubber Industry

基　　金：国家自然科学基金资助项目(20274022)

摘　　要：以富马酸二叔丁基酯和2,2-双(p-二甲基-氯硅氧基苯)丙烷为单体,通过缩聚合成得到聚[富马酸-2,2-双(p-二甲基硅氧烷-苯基)丙烷硅基酯],采用核磁共振氢谱、差示扫描量热法、热失重分析和凝胶渗透色谱表征了聚合物。结果表明,该聚合物的重均分子量为6 912,聚合度为15.6,玻璃化转变温度为16.7℃,具有良好的热稳定性,且在48 h基本降解完全。Poly（fumaric acid silyl ester） was synthesized by polycondensation of di-tert-butyl fumarate with 2,2-bis（p-chlorodimethylsiloxy-phenyl）propane.The polymer was characterized by 1H-nuclear magnetic resonance,differential scanning calorimetry,thermogravimetric analysis andgel permeation chromatography.The results showed that the weight-average molecular weight and polymerization degree were 6 912,15.6,respectively.The glass transition temperature was 16.7 ℃,and the thermal stability was good.The polymer degraded completely in 48 h.

关 键 词：富马酸二叔丁基酯 2 2-双(p-二甲基-氯硅氧基苯)丙烷 缩聚 聚硅基酯 降解 

分 类 号：TQ316.33[化学工程—高聚物工业]