含Sc和Zr的2618铝合金冷轧板材退火时组织性能的变化  

Microstructure and Hardness Changes of Cold rolled 2618 Alloy Plate with Trace Sc and Zr Addition during Annealing

作　　者：余琨[1] 李松瑞[1] 黎文献[1] 

机构地区：[1]中南工业大学材料科学与工程系,长沙410083

出　　处：《金属热处理》1999年第11期14-16,共3页Heat Treatment of Metals

摘　　要：测量了含微量Ｓｃ 和Ｚｒ 的２６１８ 铝合金冷轧板材退火时的硬度变化，用金相显微镜和透射电镜观察了合金的显微组织。结果发现加入Ｓｃ 和Ｚｒ 后，合金中生成的细小弥散的共格Ａｌ３（Ｓｃ，Ｚｒ） 质点可有效地钉扎位错，稳定亚结构，阻止晶界推移，从而抑制合金退火时再结晶的发生，对提高２６１８ 合金的耐热性能有利。The hardness variation of cold rolled 2618 alloy plate with trace Sc and Zr addition during annealing had been measured.The microstructures of alloy were observed by optical microscope and transmission electron microscopy (TEM).It was found that the dispersed Al 3(Sc,Zr) particles could pin dislocations,stabilize substructures and impede the movement of boundaries,so the recrystallization of alloy was retarded and Al 3(Sc,Zr) phase was beneficial to improve the thermal resistance properties.

关 键 词：钪 锆 再结晶 铝合金 退火 

分 类 号：TG146.21[一般工业技术—材料科学与工程] TG166.3[金属学及工艺—金属材料]