不锈钢堆焊层提高A204GrA钢的高温抗氢蚀性能研究  

The Study of Elevation Hydrogen Attack Resistance for A204GrA by Stainless Steel Weld Overlay

作　　者：秦江阳[1] 王印培[1] 柳曾典[1] 陈进[1] 

机构地区：[1]华东理工大学

出　　处：《压力容器》1999年第6期9-14,83,共7页Pressure Vessel Technology

摘　　要：本文针对Ａ２０４ＧｒＡ 钢氢腐蚀事例的增多， 试验研究了不锈钢堆焊层对Ａ２０４ＧｒＡ 钢抗高温氢腐蚀的作用， 研究结果表明： 不锈钢堆焊层使Ｎｅｌｓｏｎ 曲线中的Ａ２０４ＧｒＡ 曲线升高， 相当于提高了Ａ２０４ＧｒＡ 钢的高温抗氢蚀能力。利用以上试验结果， 分析了一台位于Ｎｅｌｓｏｎ 曲线中不安全区的Ａ２０４ＧｒＡ 钢加氢反应器，表明在不锈钢堆焊层的作用下，This paper aim at the more and more hydrogen attack for A204GrA steel,it is tested and studied that the effect of stainless steel weld overlay (SSWO) elevate the ability of hydrogen attack resistance of A204GrA.SSWO Let the Curve of A204GrA to elevate in Nelson Curve.Using above Test Results,A204GrA hydrogenator with austenitic stainless steel overlay was assessed.This hydrogenator can be safely used above 0 5Mo steel operating limit in Nelson Curve and will not be hydrogen attack during the period of inspection.

关 键 词：不锈钢堆焊层 氢蚀 抗氢钢 堆焊 

分 类 号：TG142.7[一般工业技术—材料科学与工程] TG455[金属学及工艺—金属材料]