快速凝固Cu-Zr合金的析出特性及其对性能的影响  

Precipitation Behavior and Its Effects on Properties Rapidly Solidified Cu-Zr Alloy

作　　者：刘平[1] 康布熙[2] 曹兴国[2] 黄金亮[2] 顾海澄[1] 

机构地区：[1]西安交通大学材料学院,陕西西安710049 [2]洛阳工学院材料系,河南洛阳471039

出　　处：《功能材料》1999年第6期624-626,共3页Journal of Functional Materials

基　　金：国家自然科学基金!资助项目59671043

摘　　要：本文采用透射电镜对快速凝固Ｃｕ － Ｚｒ 合金析出过程中组织的变化进行了研究。分析了时效析出过程中组织和性能的变化规律。结果表明：快速凝固Ｃｕ － Ｚｒ 合金经适当的时效处理，可以在保持高的导电率的前提下，大幅度提高合金的显微硬度。合金经５５０ ℃时效２ｈ ，其导电率为８２ ％ ＩＡＣＳ，显微硬度可达ＨＶ２３０ ，时效析出相为球状的Ｃｕ５Ｚｒ ，在峰值状态时与母相保持共格关系。The microstructure,mechanical and electrical properties of rapidly solidified (RS) Cu-Zr alloy upon aging precipitation have been investigated and analysed by using TEM.The results have shown that there are a big increase in microhardness in the premise of higher electric conductivity for RS Cu-Zr alloy.Upon aging at 550℃ for 2h,the electric conductivity remains as high as 82% IACS and the microhardness is enhanced to about Hv230.The aging precipitates are globular Cu 5Zr,which keeps coherent with the matrix.

关 键 词：铜锆合金 快速凝固 时效析出 共格关系 

分 类 号：TG146.11[一般工业技术—材料科学与工程]