表面处理剂对隔热层粘接性能的研制  

The Effect of Surface Treatment Agent on the Adhesion Properties of Heat-insulating Layer

作　　者：王勃[1] 黄伣丽[1] 曹先启[1] 陈泽明[1] 王超[1] 

机构地区：[1]黑龙江省科学院石油化学研究院,黑龙江哈尔滨150040

出　　处：《化学与粘合》2011年第3期15-16,共2页Chemistry and Adhesion

摘　　要：为提高隔热层粘接强度,采用材料拉伸强度测试方法,研究了空气湿度、处理剂浓度对常温固化磷酸盐胶黏剂粘接隔热层力学性能的影响。研究表明,当处理剂浓度为5%,空气湿度为70%,处理剂处理的隔热层可以在20～1200℃达到隔热层深层破坏,而且粘接强度还得到较大提高,表明该处理剂可以显著提高隔热层的粘接强度。In order to enhance the bonding strength of heat-insulating layer, the effect of humidity and concentration of treatment agent on the mechanical property of heat-insulating layer bonded with normal temperature curing phosphate adhesive were research with adopting material tensile strength testing method. The results indicated that when the humidity was 70% and the concentration of treatment agent was 5%, the heat-insulating layer treated by the agent could be destroyed deeply at 20-1200℃, and the bending strength was improved greatly, it was proved that this surface treatment agent could remarkably enhance the bonding strength of heat-insulating layer.

关 键 词：处理剂 隔热层 粘接 

分 类 号：TQ437.4[化学工程]