重油催化裂化脱硫系统换热器的电偶腐蚀  

Galvanic Corrosion of Heat Exchangers of Desulf urization System of Heavy Oil Catalytic Cracking

作　　者：毛庆斌[1] 邓春光[1] 张林[1] 唐同庆 

机构地区：[1]武汉石油化工厂设备研究所,湖北省武汉市430082

出　　处：《石油化工腐蚀与防护》1999年第2期20-24,共5页Corrosion & Protection In Petrochemical Industry

摘　　要：利用金相和电化学方法分析了武汉石油化工厂脱硫系统换热器管束腐蚀穿孔的原因,认为碳钢换热器防冲板和管束的穿孔主要是由于沉积物的堆积而产生的电偶腐蚀所致.提出改进防冲板设计,对溶液进行过滤和降低溶液中的氧含量等措施可减少或避免这种类型的腐蚀.The causes of heat exchanger tube failure in the desul-furization system of heavy oil FCC in Wuhan Petrochemical Plant were analyzed. It was concluded that the failure of the impingement plate and tubes was caused by the galvanic corrosion by the build-up of deposit. The improvement of impingement plate design, filtration and reduction of oxygen content of solution, etc. were suggested to mitigate and avoid the corrosion.

关 键 词：脱硫系统 碳钢 换热器 重油 催化裂化 电偶腐蚀 

分 类 号：TE985.9[石油与天然气工程—石油机械设备]