硅烷偶联剂改性ATT的制备及其对Cr^(6+)吸附性能的研究  

Preparation of Silane Coupling Agent Modified Attapulgite and Adsorption Property of Cr^(6+)

作　　者：朱维菊[1] 高华[1] 李村[1] 吴振玉[1] 方敏[1] 

机构地区：[1]安徽大学化学化工学院,安徽合肥230039

出　　处：《非金属矿》2011年第3期64-67,共4页Non-Metallic Mines

基　　金：安徽高校省级自然科学研究项目(KJ2009A103);安徽省自然科学研究项目(11040606M33)

摘　　要：采用硅烷偶联剂KH-550对盐酸改性凹凸棒土(HATT)进行有机改性,以制备改性凹凸棒土吸附材料(OHATT)。通过氮吸附比表面及孔结构分析、红外光谱、XRD等手段对改性凹凸棒土进行了表征;研究了改性凹凸棒土对Cr6+的吸附性能,并考察不同制备条件对OHATT吸附Cr6+的影响。研究结果表明,改性剂用量为(相对HATT质量)1%、反应时间为4 h、反应温度为50℃时,制备的OHATT对Cr6+的吸附容量最大。OHATT adsorbent was synthesized by grafting silane coupling agent KH-550 onto the hydrochloric acid modified ATT （HATT）. Thermal behavior and the structure of OHATT were characterized by TGA, DSC, FTIR, XRD and BET. The results showed that the KH-550 was successfully grafted onto the HATT surface. Preparing conditions of the OHATT were investigated. The results showed that the OHATT prepared under silane coupling agent mass concentration 1% （relative to,HATT mass） at 50℃ for 4h gave a maximum Cr6＋ adsorption capacity.

关 键 词：凹凸棒土 硅烷偶联剂 改性 吸附 Cr6+ 

分 类 号：TD975[矿业工程—选矿] X703[环境科学与工程—环境工程]