腐蚀产物膜对氨基乙酸缓蚀性能的影响  

Effect of corrosion film on corrosion inhibition of glycine

作　　者：高延敏[1] 杨洁[1] 李晓伟[1] 

机构地区：[1]江苏科技大学材料科学与工程学院,江苏镇江212003

出　　处：《江苏科技大学学报（自然科学版）》2011年第2期136-139,共4页Journal of Jiangsu University of Science and Technology:Natural Science Edition

基　　金：江苏省研究生科研创新基金资助项目(CX07S-024z)

摘　　要：为了探索腐蚀产物膜对缓蚀剂性能的影响,利用SEM,XRD,极化曲线及交流阻抗技术研究了NaHCO3溶液中腐蚀产物膜结构和成分改变对缓蚀剂性能的影响.结果表明:加入不同离子后,腐蚀产物膜的成分及结构发生了明显的变化;在腐蚀介质浓度为40 g/L时,由于所形成的主要成分为FeCO3的腐蚀产物膜组织结构致密均匀,缓蚀剂氨基乙酸能很好地吸附在腐蚀产物膜上,通过影响阳极钝化区提高了金属抗腐蚀的能力.In order to explore the influence of corrosion film to corrosion inhibitor,the effects of structure and component change of corrosion film on corrosion inhibitors are researched by SEM,XRD,polarization curves and impedance.Results indicate that the component and structure change after adding different ions.In the medium concentration of 40 g/L,the structure of corrosion film that is mainly composed of FeCO3 is dense and uniform,and glycine has good adsorption on the surface of corrosion film.This leads to a good capacity to suppression of metal corrosion by affecting anodic passive area.

关 键 词：腐蚀产物膜 氨基乙酸 交流阻抗 

分 类 号：TG174.42[金属学及工艺—金属表面处理]