La-Zn替代对永磁铁氧体磁粉结构与性能的影响  

Effect of La-Zn substitution on the microstructure and properties of Sr-ferrite powders

作　　者：连江滨[1,2] 吕宝顺[1] 廖有良[1] 邹科[1] 熊凌云[1] 

机构地区：[1]北矿磁材科技股份有限公司,北京100074 [2]清华大学材料科学与工程系,北京100084

出　　处：《磁性材料及器件》2011年第3期53-55,67,共4页Journal of Magnetic Materials and Devices

摘　　要：采用传统陶瓷工艺制备注射成型用的Sr1-xLaxFe12-xZnxO19磁粉,研究了La、Zn替代对磁粉结构、组织、粉体特性和注射成型磁体性能的影响。结果表明,La、Zn替代将抑制晶粒长大,提高磁粉Hcj,但导致磁粉压缩密度下降,当x=0.2时,磁粉的Hcj获得最大值;La、Zn元素的少量替代有利于提高注射成型磁体的Br。Sr1-xLaxFe12-xZnxO19（0≤x≤0.3） ferrite powder for injection molded magnet was prepared using conventional ceramic process,and the effect of La-Zn substitution on the microstructure and properties of Sr1-xLaxFe12-x ZnxO19（0≤x≤0.3） powder and bonded magnet from it was investigated.Research showed that La-Zn substitution can restrain the crystal growth and resultantly improve Hcj,but result in decreasing of packing density.Optimum Hcj was achieved for x=0.2 sample.Small part of La-Zn substitution would be beneficial to improve the Br of injection molded magnet.

关 键 词：锶铁氧体 La-Zn替代 磁粉 注射成型 

分 类 号：TM273[一般工业技术—材料科学与工程]