NANOPOROUS MATERIALS BASED ON SPIROKETAL AND SPIROTHIOKETAL POLYMERS FOR SEPARATING METHANOL-TOLUENE MIXTURE  

作　　者：Hamada Hamada Abdel-Razik Zeinhom Mohamed El-Bahy 

机构地区：[1]Chemistry Department,Faculty of Science and Education(Alkhurma Branch),Taif University,Saudi Arabia

出　　处：《Chinese Journal of Polymer Science》2011年第4期450-455,共6页高分子科学（英文版）

摘　　要：Organic microporous materials based on spiroketal and spirothioketal polymers were synthesized through 1,3- dioxol-forming polymerization reaction between pentaerythritol or pentaerythritol tetrathiol and different types of cyclohexa- 1,4-dione derivatives. The structure of the prepared polymers was confirmed by NMR spectroscopy and molecular mass measurements. Nitrogen adsorption/desorption isotherms of the prepared polymers show a large amount of nitrogen adsorbed at low relative pressure indicating microporosity. These polymers have Brunauer Emmitt and Teller （BET） surface areas in the range from 492 （m^2g^-1） to 685 （m^2 g^-1）. The prepared polymers were found to be useful for pervaporation separation of methanol-toluene mixture with a separation factor up to 12.5 and fluxes, varying between 6.7×10-3 kg/（m^2 h） and 13.4 × 10^-3 kg/（m^2 h）.Organic microporous materials based on spiroketal and spirothioketal polymers were synthesized through 1,3- dioxol-forming polymerization reaction between pentaerythritol or pentaerythritol tetrathiol and different types of cyclohexa- 1,4-dione derivatives. The structure of the prepared polymers was confirmed by NMR spectroscopy and molecular mass measurements. Nitrogen adsorption/desorption isotherms of the prepared polymers show a large amount of nitrogen adsorbed at low relative pressure indicating microporosity. These polymers have Brunauer Emmitt and Teller （BET） surface areas in the range from 492 （m^2g^-1） to 685 （m^2 g^-1）. The prepared polymers were found to be useful for pervaporation separation of methanol-toluene mixture with a separation factor up to 12.5 and fluxes, varying between 6.7×10-3 kg/（m^2 h） and 13.4 × 10^-3 kg/（m^2 h）.

关 键 词：Spiroketal polymers Nanoporous materials Separation membranes. 

分 类 号：TB383.1[一般工业技术—材料科学与工程]