氢对2(1/4)Cr-1Mo钢力学性能的影响  

EFFECT OF HYDROGEN ON MECHANICAL PROPERTIES FOR 2(1/4)Cr-1Mo STEEL

作　　者：钟曼英[1] 

机构地区：[1]中国计量学院机电学院,杭州310018

出　　处：《中国腐蚀与防护学报》2011年第3期236-239,共4页Journal of Chinese Society For Corrosion and Protection

摘　　要：在模拟加氢反应器工况条件下,研究氢对加氢反应器器壁材料2(1/4)Cr-1Mo钢的力学性能的影响。采用低周疲劳实验计算原始状态和渗氢试样的裂纹扩展速率da/dN及门槛值△J_(th);并测试裂纹尖端附近的氢分布。结果表明,氢含量与应力场有关,应力越大氢含量就越高。假设在反应器壁内存在表面裂纹的情况下,估算了加氢反应器的剩余寿命。The effect of hydrogen on the mechanical properties for 2（1/4）Cr-1Mo steel for hydrogenation reactor wall-materials was investigated at the simulated service condition of hydrogenation reactor. Tile crack propagation rate da/dN and the threshold value△Jth at low frequency fatigue were calculated. Hydrogen distribution of crack tip were measured. The results showed that hydrogen content related to stress field. The higher the stress, the higher the hydrogen content. The residual cycle life for hydrogenation reactor was calculated, supposing surface crack exists in reactor.

关 键 词：2(1/4)Cr-1Mo钢 力学性能 裂纹扩展速率da/dN 氢分布 剩余寿命 

分 类 号：TG113.25[金属学及工艺—物理冶金]