Fabrication and Magnetic Properties of Composite Ni_(0.5)Zn_(0.5)Fe_2O_4/Pb(Zr_(0.52)Ti_(0.48))O_3 Nanofibers by Electrospinning  

作　　者：沈湘黔 

机构地区：[1]School of Materials Science and Engineering,Jiangsu University

出　　处：《Journal of Wuhan University of Technology(Materials Science)》2011年第3期384-387,共4页武汉理工大学学报（材料科学英文版）

基　　金：Funded by the National Natural Science Foundation of China (No. 50674048);Research Fund for the Doctoral Program of Higher Education of China(No.20103227110006)

摘　　要：One-dimensional and quasi-one-dimensional nanostructure materials are promising building blocks for electromagnetic devices and nanosystems.In this work,the composite Ni0.5Zn0.5Fe2O4（NZFO）/ Pb（Zr0.52Ti0.48）O3（PZT） nanofibers with average diameters about 65 nm are prepared by electrospinning from poly（vinyl pyrrolidone） （PVP） and metal salts.The precursor composite NZFO/PZT/PVP nanofibers and the subsequent calcined NZFO/PZT nanofibers are investigated by Fourier transform infrared spectroscopy （FT- IR） ,X-ray diffraction （XRD）,scanning electron microscopy （SEM）.The magnetic properties for nanofibers are measured by vibrating sample magnetometer（VSM）.The NZFO/PZT nanofibers obtained at calcination temperature of 900 °C for 2 h consist of the ferromagnetic spinel NZFO and ferroelectric perovskite PZT phases,which are constructed from about 37 nm NZFO and 17 nm PZT grains.The saturation magnetization of these NZFO/PZT nanofibers increases with increasing calcination temperature and contents of NZFO in the composite.One-dimensional and quasi-one-dimensional nanostructure materials are promising building blocks for electromagnetic devices and nanosystems.In this work,the composite Ni0.5Zn0.5Fe2O4（NZFO）/ Pb（Zr0.52Ti0.48）O3（PZT） nanofibers with average diameters about 65 nm are prepared by electrospinning from poly（vinyl pyrrolidone） （PVP） and metal salts.The precursor composite NZFO/PZT/PVP nanofibers and the subsequent calcined NZFO/PZT nanofibers are investigated by Fourier transform infrared spectroscopy （FT- IR） ,X-ray diffraction （XRD）,scanning electron microscopy （SEM）.The magnetic properties for nanofibers are measured by vibrating sample magnetometer（VSM）.The NZFO/PZT nanofibers obtained at calcination temperature of 900 °C for 2 h consist of the ferromagnetic spinel NZFO and ferroelectric perovskite PZT phases,which are constructed from about 37 nm NZFO and 17 nm PZT grains.The saturation magnetization of these NZFO/PZT nanofibers increases with increasing calcination temperature and contents of NZFO in the composite.

关 键 词：nanofiber Ni0.5Zn0.5Fe2O4 Pb（Zr0.52Ti0.48）O3 composite electrospinning 