高砷低品位金矿的提金实验研究  

Study on Gold Extraction from a Low-grade High-arsenic-containing Gold Ore

作　　者：朱军[1] 王毅[1] 祁栋[1] 刘漫博[1] 刘苏宁[1] 

机构地区：[1]西安建筑科技大学,陕西西安710055

出　　处：《矿冶工程》2011年第3期81-84,88,共5页Mining and Metallurgical Engineering

摘　　要：研究了高砷低品位金矿采用焙烧预处理进行氰化提金的工艺。以CaCO3作为焙烧固定剂,Pb(NO3)2作为助浸剂,最佳实验条件为:磨矿粒度为-0.074 mm粒级占90%,焙烧时间4 h,CaCO3用量为矿量的2%,焙烧温度650℃;助浸剂Pb(NO3)2用量200 g/t,预处理4 h,NaCN用量1.2 kg/t,浸出时间22 h,浸出温度20℃,pH=11,液固比2.5,搅拌速度900 r/min,此条件下金的浸出率达到80.67%。The process for gold recovery with Cyanide from a low-grade high-arsenic-containing gold deposit by roasting pretreatment was studied.It is concluded that choosing CaCO3 as a fixing agent for roasting,Pb（NO3）2 as leaching agent,the gold leaching rate can be 80.67% under the following optimum conditions： with 90% particles of-0.074 mm grinding size,being roasted at a temperature of 650 ℃ for 4 hrs with dosage of CaCO3 2% of the ore feed and 1.2 kg/t of leaching agent Pb（NO3）2,pretreated for 4 h with 1.2 kg/t of NaCN,leaching at a temperature of 20 ℃ for 22 h from a solution with pH=11,liquid-solid ratio of 2.5 at a mixing speed of 900 r/min.

关 键 词：氰化提金 低品位金矿 焙烧固定剂 助浸剂 浸出率 

分 类 号：TF111[冶金工程—冶金物理化学]