H08Mn2Si钢高速线材控轧控冷试验  

Testing on Controlled Rolling and Cooling of High Speed Rolled Wire of Steel H08Mn2Si

作　　者：冯贺滨[1] 王有铭[1] 刘明哲[2] 李克敏[2] 褚建东[2] 

机构地区：[1]北京科技大学,北京100083 [2]唐山钢铁(集团)公司

出　　处：《特殊钢》1999年第6期13-15,共3页Special Steel

摘　　要：研究了生产H08Mn2Si 高速线材控轧控冷工艺参数,分析了终轧温度和冷却速率对力学性能的影响,得出最佳工艺为终轧温度850 ℃,760 ～580 ℃之间的冷却速度< 1 ℃/s。The process parameters of controlled rolling and cooling for high speed rolling wire production of steel H08Mn2Si has been tested. The optimum process parameters : temperature of finished rolling\|850 ℃ and cooling rate from 760\C to 580\C \| <1\C/s have been obtained.Abstract The process parameters of controlled rolling and cooling for high speed rolling wire production of steel H08Mn2Si has been tested. The optimum process parameters : temperature of finished rolling\|850 ℃ and cooling rate from 760\C to 580\C \| <1\C/s have been obtained.

关 键 词：热模拟试验 高速线材 控制轧制 控制冷却 

分 类 号：TG335.63[金属学及工艺—金属压力加工]