静电纺丝法制备的多孔碳纳米纤维  被引量:4

Porous carbon nanofibers prepared by electrospinning technique

在线阅读下载全文

作  者:李静[1] 乔辉[1] 魏取福[1] 

机构地区:[1]江南大学纺织服装学院,生态纺织教育部重点实验室,江苏无锡214122

出  处:《电池》2011年第3期132-134,共3页Battery Bimonthly

基  金:中央高校基本科研业务费专项资金(JUSRP11102);江苏省自然科学基金(BK2010140)

摘  要:用静电纺丝法制备了聚丙烯腈(PAN)/聚甲基丙烯酸甲酯(PMMA)复合纳米纤维,经预氧化、高温炭化,制备用作锂离子电池负极材料的碳纳米纤维(CNF)。透射电子显微镜(TEM)和比表面积分析发现:制备的CNF具有多孔结构,比表面积达到572.9 m^2/g,平均孔径为33.6 nm。以50 mA/g的电流在0.01-3.00 V循环,制备的多孔CNF的首次放电比容量为333.3 mAh/g,第20次循环的可逆比容量为231.8 mAh/g,充放电效率近90%。Polyacrylonitrile(PAN)/poly(methyl methacrylate)(PMMA) composite nanofibers were prepared by electrospinning technique,then porous carbon nanofibers(CNF) as anode material for Li-ion battery were obtained by pre-oxidation and high temperature carbonation.The analyses of transmission electron microscopy(TEM) and specific surface area showed that the as-prepared CNF had porous structure,the specific surface area was 572.9 m2/g,the mean pore size was 33.6 nm.When cycled in 0.01~3.00 V with the current of 50 mA/g,the initial specific discharge capacity of the as-prepared porous CNF was 333.3 mAh/g,the reversible specific capacity was 231.8 mAh/g at the 20th cycle,the charge-discharge efficiency was near 90%.

关 键 词:静电纺丝法 碳纳米纤维(CNF) 多孔结构 负极材料 充放电性能 

分 类 号:TM912.9[电气工程—电力电子与电力传动]

 

参考文献:

正在载入数据...

 

二级参考文献:

正在载入数据...

 

耦合文献:

正在载入数据...

 

引证文献:

正在载入数据...

 

二级引证文献:

正在载入数据...

 

同被引文献:

正在载入数据...

 

相关期刊文献:

正在载入数据...

相关的主题
相关的作者对象
相关的机构对象