GAP基热塑性弹性体的合成与表征  

Synthesis and Characterization of GAP-based Thermoplastic Elastormer

作　　者：宋晓庆[1] 王文浩[1] 周集义[1] 白森虎[1] 

机构地区：[1]黎明化工研究院,河南洛阳471000

出　　处：《化学推进剂与高分子材料》2011年第4期70-72,共3页Chemical Propellants & Polymeric Materials

摘　　要：以聚叠氮缩水甘油醚(GAP)、亚甲基二苯基二异氰酸酯(MDI)、1,4–丁二醇(BDO)为原料,采用两步法合成了一种GAP基的含能热塑性弹性体(ETPE)。用差示扫描量热(DSC)、傅里叶变换红外光谱(FT–IR)、热失重(TG)和万能材料拉伸机等对ETPE进行了表征。结果表明,ETPE具有良好的低温性能和热稳定性,高相对分子质量的GAP所制得的ETPE具有优异的断裂伸长率。A GAP-based energetic thermoplastic elastomer（ETPE） was synthesized by two-step method using glycidyl azide polymer（GAP）,methylene diphenylene isocyanate（MDI） and 1,4-butanediol（BDO） as raw merterials.The ETPE was characterized by differential scanning calometry（DSC）,Fourier transform infrared spectrometry（FT-IR）,thermogravimetry（TG）,universal material tension tester,etc.The results show that the ETPE has better low temperature properties and thermal stability,and the ETPE prepared from high relative molecular mass GAP has excellent elongation at break.

关 键 词：GAP 含能 热塑性弹性体 

分 类 号：TQ334[化学工程—橡胶工业]