以环己烷为前驱体制备炭/炭复合材料  

Preparation of carbon/carbon composites by chemical liquid-vaporized infiltration process with cyclohexane as precursor

作　　者：王万平 赵建国[1,2] 

机构地区：[1]方大炭素新材料科技股份有限公司博士后工作站,甘肃兰州730084 [2]山西大同大学炭材料研究所,山西大同037009

出　　处：《炭素技术》2011年第3期6-9,共4页Carbon Techniques

基　　金：国家自然科学基金(51072105);中国博士后科学基金资助项目(20100480727)

摘　　要：以环己烷为前驱体利用化学液气相沉积工艺,采用针刺炭纤维毡为预制体,制备了具有光滑层和粗糙层结构的炭/炭复合材料。利用金相显微镜、高分辨扫描电子显微镜进行了材料的微观组织结构的分析,分析了在不同位置不同织构热解炭的形成机理。同时阐述了化学液气相沉积工艺原理。实验结果表明,通过调整工艺参数,利用化学液气相沉积工艺可以制备具有不同微观组织结构的炭/炭复合材料。Carbon/carbon composites with the rough laminar and smooth laminar pyr ocarbons were prepared by chemical liquid-vaporized infiltration process with c yclohexane as the precursor and the needled carbon fiber felt as the preform.Th e microstructure of pyrocarbon at different positions was measured and discussed .The principle of chemical liquid-vaporized infiltration technology was illumi nated.The results indicate that different microstructures of pyrocarbons can be obtained by changing the parameters of the process.

关 键 词：化学液气相沉积 环己烷 热解炭 炭/炭复合材料 

分 类 号：TB332[一般工业技术—材料科学与工程] TQ342.742[化学工程—化纤工业]