缓释型重组人骨形态发生蛋白2/壳聚糖生物骨修复材料诱导骨形成  

Enhancement of bone formation by recombinant human bone morphogenetic protein-2/chitosan bone biomaterials

作　　者：王丁丁[1] 曾戎[2] 杨敏儿[1] 何鉴贤[1] 陈阳[3] 何水连[3] 陈安安[3] 周智优[3] 袁丽颖[4] 汪炬[3] 

机构地区：[1]广东药学院生命科学与生物制药学院,广东省广州市510006 [2]暨南大学材料科学与工程系,广东省广州市510632 [3]暨南大学生命科学技术学院,广东省广州市510632 [4]吉林大学附属第三幼儿园,吉林省长春市130021

出　　处：《中国组织工程研究与临床康复》2011年第25期4583-4586,共4页Journal of Clinical Rehabilitative Tissue Engineering Research

基　　金：广东省科技攻关项目(2009B030801237);广东省教育部科技部企业科技特派员行动计划项目(2009B090600134);国家自然科学基金青年基金项目(81000923)~~

摘　　要：背景:重组人骨形态发生蛋白2在体内半衰期短、易降解代谢,达不到理想的骨再生效果。目的:制备缓释型重组人骨形态发生蛋白2/壳聚糖生物骨修复材料,并观察其缓释性能、骨诱导活性。方法:将重组人骨形态发生蛋白2与壳聚糖混合制备壳聚糖膜,涂覆于生物骨修复材料表面,ELISA方法检测其体外释药性能。茜素红染色检测缓释型人骨形态发生蛋白2/壳聚糖生物骨材料、重组人骨形态发生蛋白2生物骨材料、单纯骨填充材料诱导C2C12细胞骨钙蛋白的形成,观察其诱导成骨细胞能力。同时将3种骨修复材料植入清洁级KM小鼠股部肌袋内,2周后检测新生骨Ca2+离子含量,评价其异位骨诱导能力。结果与结论:材料表面的壳聚糖膜分布均匀,负载的重组人骨形态发生蛋白2呈团簇状。重组人骨形态发生蛋白2/壳聚糖生物骨修复材料体外释药存在突释,前4d释放量达总药量的50%,持续至12d,释药量达到90%,第18天时释放完全。与单纯骨填充材料、重组人骨形态发生蛋白2生物骨材料相比,缓释型人骨形态发生蛋白2/壳聚糖生物骨修复材料诱导C2C12细胞向成骨晚期分化能力与异位骨形成能力显著增强(P<0.05)。结果提示缓释型人骨形态发生蛋白2/壳聚糖生物骨修复材料缓释性能好,促进骨形成能力强。BACKGROUND：The recombinant human bone morphogenetic protein-2（rhBMP-2） administered in solution often loses its bioactivity in a short time and does not always exhibit efficacy required in bone regeneration in vivo.It would be ideal to develop a system for the sustained delivery of biologically active rhBMP-2 over an extended period of time.OBJECTIVE：To evaluate rhBMP-2 sustained delivery and osteoinductive effects of bone biomaterials which were combined with chitosan films containing rhBMP-2.METHODS：①The rhBMP-2 was added into a chitosan solution to prepare chitosan films which were spread on the bone materials.The effect of slow release was analyzed by ELISA assays.②In vitro,the osteoinductive to differentiation marker（osteocalcin） of C2C12 cells after induction of rhBMP-2/chitosan（CS） bone biomaterials was assayed by Alizarin red staining.③Intramuscular implantation test was made in vivo,rhBMP-2/CS carriers were implanted in muscles of the hind leg of rat for two weeks.The amount of calcium deposited in the implants was measured to assay bioactivity.RESULTS AND CONCLUSION：①A scanning electron micrograph of the rhBMP-2/CS bone biomaterials showed uniform distribution of chitosan films on the material surface with rhBMP-2 scattering like cluster.②An abrupt rhBMP-2 release from rhBMP-2/CS carriers was observed.50% of the loaded rhBMP-2 was released in 4 days.Thereafter,the release rate was nearly constant until day 12 when 90% of rhBMP-2 was released.All of it was released by day 18 at last.③In vitro rhBMP-2 released from the rhBMP-2/CS carriers stimulated an increase in osteocalcin of C2C12 cells after 4 weeks.④In vivo bone formation studies showed the rhBMP-2/CS biomaterials induced bone formation to a much greater extent than control groups by Ca2＋ test assay.These results demonstrate that the rhBMP-2/CS bone biomaterials delivery system is capable of potentiating the osteogenic efficacy of rhBMP-2 and underscore its importance as a possible bone regeneration strategy.

关 键 词：人骨形态发生蛋白2 壳聚糖 缓释 骨修复材料 骨形成 