淬火温度对薄片类小零件脆性和弹性的影响  

Influence of Quenching Temperature on Elasticity and Brittleness of Thin Small Parts

作　　者：张莉[1] 丁浩[1] 严晶晶[1] 朱世根[1] 

机构地区：[1]东华大学机械工程学院纺织装备教育部工程研究中心,上海201620

出　　处：《热加工工艺》2011年第14期143-145,共3页Hot Working Technology

基　　金：国家科技支撑计划"新一代纺织设备"重点基金资助项目(2007BAF24B04-4)

摘　　要：研究了淬火温度对含碳量为0.9%～1.0%的ZK钢薄片小零件脆性和弹性的影响。结果表明:在本试验范围内,若淬火温度较低,由于非马氏体组织的存在,弹性很差;若淬火温度较高,由于粗大马氏体的存在,脆性很大;对于薄片类小零件,淬火时从离开炉膛到落入油槽下落过程的温度降低不容忽视,加热温度应略高于淬火温度。The influences of quenching temperature on the elasticity and brittleness of thin small parts（wC=0.9%～1.0%） were investigated.The results show that the elasticity decreases when the parts are quenched at lower temperature in the reason of the pearlite.On the other hand,the parts might become more brittle at higher quenching temperature because of the coarse martensite.The descent of temperature is unignorable while the parts fall down from the furnace hearth to the quenching oil surface.The heating temperature should be a little higher than the quenching temperature.

关 键 词：薄片小零件 淬火温度 弹性 脆性 

分 类 号：TG156.3[金属学及工艺—热处理]