POLYMERIZATION OF 1-OCTENE AND DETERMINATION OF MARKHOUWINK CONSTANTS OF POLY(1-OCTENE)  

作　　者：付志峰 

机构地区：[1]State Key Laboratory of Chemical Resource Engineering,Beijing University of Chemical Technology

出　　处：《Chinese Journal of Polymer Science》2011年第5期560-568,共9页高分子科学（英文版）

基　　金：supported by the program for new century excellent talents in Chinese universities and Beijing Municipal Education Commission

摘　　要：The polymerization of 1-octene initiated by methylalmnoxane （MAO）-activated Ni（II）-based-a-diimine complexes [（2,6-i-Pr）2C6H3-DAB（An）]NiBr2 was investigated. Using this catalyst, poly（1-octene）s with molecular weight between 100 × 10^3 and 400 ×10^3 and polydispersity （Mw/Mn） between 1.3 and 1.5 were synthesized successfully by varying reaction time at room temperature. The poly（1-octene）s were amorphous polymers and could be well soluble in tetrahydrofuran （THF）. After fractional precipitation, poly（1-octene）s with narrow molecular weight distributions （Mw/Mn 〈 1.12） were obtained. Their weight-average molecular weights were measured by gel permeation chromatography （GPC） in conjunction with online model BI-MwA multiangle laser light scattering （MALLS）, and their intrinsic viscosities were measured by Maron＇s single-point method. The k and a values in Mark-Houwink equation [η] = KM^a in THF at 40α were 0.089 mL/g and 0.61 respectively.The polymerization of 1-octene initiated by methylalmnoxane （MAO）-activated Ni（II）-based-a-diimine complexes [（2,6-i-Pr）2C6H3-DAB（An）]NiBr2 was investigated. Using this catalyst, poly（1-octene）s with molecular weight between 100 × 10^3 and 400 ×10^3 and polydispersity （Mw/Mn） between 1.3 and 1.5 were synthesized successfully by varying reaction time at room temperature. The poly（1-octene）s were amorphous polymers and could be well soluble in tetrahydrofuran （THF）. After fractional precipitation, poly（1-octene）s with narrow molecular weight distributions （Mw/Mn 〈 1.12） were obtained. Their weight-average molecular weights were measured by gel permeation chromatography （GPC） in conjunction with online model BI-MwA multiangle laser light scattering （MALLS）, and their intrinsic viscosities were measured by Maron＇s single-point method. The k and a values in Mark-Houwink equation [η] = KM^a in THF at 40α were 0.089 mL/g and 0.61 respectively.

关 键 词：Nickel（a-diimine） catalyst Poly（1-octene） Mark-Houwink constants. 

分 类 号：O631.3[理学—高分子化学]