Evaluation of reclaimed asphalt pavement binder stiffness without extraction and recovery  

作　　者：马涛 黄晓明 U.B.Hussain 

机构地区：[1]School of Transportation,Southeast University [2]Department of Civil and Environmental Engineering,University of Wisconsin-Madison

出　　处：《Journal of Central South University》2011年第4期1316-1320,共5页中南大学学报（英文版）

基　　金：Project(200831800044) supported by the Ministry of Communication of China;Project(50878054) supported by the National Natural Science Foundation of China;Project(06Y31) supported by the Department of Communication of Zhejiang Province,China

摘　　要：A new testing procedure to estimate the low-temperature stiffness of the reclaimed asphalt pavement （RAP） binder was developed. In the testing procedure, the SuperpaveTM Bending Beam Rheometer （BBR） with special modifications and binder blending charts by Asphalt Institute were utilized. Modifications involved the development of a new kind of sample mold and different testing parameters were made to BBR testing procedure to capture the theological properties of bitumen mortars produced by mixing fresh binder with fine RAP materials or RAP aggregate. The stiffness relationship between binder and bitumen mortar was established based on the BBR test results. The blended binder stiffness in bitumen RAP mortar was estimated from the RAP mortar stiffness based on the binder-mortar relationship. And finally, the RAP binder stiffness was estimated from the blended binder and fresh binder stiffness based on the blending charts by Asphalt Institute. The results indicate that the new procedure can capture the rheological properties of bitumen mortar and can be used to estimate the low temperature stiffness of RAP binder without binder extraction and/or any chemical treatments.A new testing procedure to estimate the low-temperature stiffness of the reclaimed asphalt pavement(RAP) binder was developed.In the testing procedure,the SuperpaveTM Bending Beam Rheometer(BBR) with special modifications and binder blending charts by Asphalt Institute were utilized.Modifications involved the development of a new kind of sample mold and different testing parameters were made to BBR testing procedure to capture the rheological properties of bitumen mortars produced by mixing fresh binder with fine RAP materials or RAP aggregate.The stiffness relationship between binder and bitumen mortar was established based on the BBR test results.The blended binder stiffness in bitumen RAP mortar was estimated from the RAP mortar stiffness based on the bindermortar relationship.And finally,the RAP binder stiffness was estimated from the blended binder and fresh binder stiffness based on the blending charts by Asphalt Institute.The results indicate that the new procedure can capture the rheological properties of bitumen mortar and can be used to estimate the low temperature stiffness of RAP binder without binder extraction and/or any chemical treatments.

关 键 词：aged binder reclaimed asphalt pavement MORTAR STIFFNESS Bending Beam Rheometer blending chart 