核电叶轮用双相不锈钢热处理工艺研究  

INVESTIGATION ON HEAT TREATMENT OF A DUPLEX STAINLESS STEEL FOR NUCLEAR POWER PLANT IMPELLER

作　　者：梁田[1] 康秀红[1] 胡小强[1] 李殿中[1] 

机构地区：[1]中国科学院金属研究所沈阳材料科学国家(联合)实验室,沈阳110016

出　　处：《金属学报》2011年第7期921-926,共6页Acta Metallurgica Sinica

基　　金：中国科学院金属研究所沈阳材料科学国家(联合)实验室不锈钢基础问题研究资助项目KGCX2-YW-221~~

摘　　要：针对核电海水循环泵叶轮用双相不锈钢材料,研究了不同时效温度、时间及固溶后不同冷却速率对双相不锈钢组织和力学性能的影响,结果表明,在800-850℃保温5 min或冷却速率低于7.5℃/min时,材料的冲击韧性和延伸率急剧下降.OM,SEM和冲击断口观察及XRD分析证实,σ相的析出对力学性能有破坏性影响.且随着时效时间的延长,σ相变得粗大。Effects of heat treatment on microstructure and mechanical property of a cast duplex stainless steel used as making impeller of seawater circular pump in nuclear power plant were investigated. The results demonstrate that the impact energy and elongation decrease sharply when heat-treated time was longer than 5 min at 800--850 ℃ or when the cooling rate was less than 7.5 ℃/min. The σphases have been identified through SEM and XRD. The weakness of the mechanical properties is attributed to the precipitation of σphase. With increasing aging time, the σphase coarsened and the nucleation position moved from the γ/δ interfaces into the whole ferrite phase.

关 键 词：双相不锈钢 热处理 力学性能 Σ相 

分 类 号：TG142.71[一般工业技术—材料科学与工程] TG156[金属学及工艺—金属材料]